The popular type of furnace used for the production of E glass is the unit furnace. More than 10 kinds of refractories are used to build to the furnace.

Fused cast AZS block

Fused cast AZS 33# is mainly used in the burner block of the melting zone and the feeder block.

Dense chromium oxide brick

Dense chromium oxide brick has the best resistance to the corrosion by E glass. It almost causes no pollution to the glass liquid. It is ideal for the E glass furnace. It is made by isostatic pressing. It has a very dense structure. It contains more than 94% Cr2O3 and less than 15% pores and its bulk density is 4.24g/cm3. Its erosion loss is only 1/10 of that of the dense zircon brick. It is mainly used in the high temperature glass-contact areas, such as the sidewall and the tank bottom of the melting zone and the sidewall of the main channel and transition channel.

Dense zircon brick

The resistance of Dense zircon brick to high temperature and E glass is not as good as dense chromium oxide brick. It is made by isostatic pressing too. It contains more than 65% ZrO2 and less than 2.0% pores and its bulk density is 4.25g/cm3. If the operating temperature exceeds 1370℃, it will be eroded. It is mainly used as the bottom block in the lower temperature parts of the melting zone and the forming channel and transition channel, flow block and back-up block.

Zircon brick

Zircon brick contains 66% ZrO2 and its bulk density is 3.7g/cm3. It has good thermal stability and good creep resistance. Its is the sidewall and breast wall of the feeder port where the erosion of batches is severe, peep hole and the breast wall, crown and burner of the flame space of the channel.

Sintered mullite brick

Sintered mullite brick contains more than 74% Al2O3;2.2% SiO2 and its bulk density is 2.5g/cm3. It is generally used as the back-up brick of the zircon brick, the breast wall and front wall of the melting zone, the lining brick of the flue of the channel, the foot parts of the crown and the outside layer of the discharging port

There is another type of mullite brick which is made by melting the raw materials first to form mullite crystals and then sintering it. It has better resistance to creep and thermal shock than mullite brick. It can be used in the crown and the breast wall of the flame space.

Fused cast mullite brick

Fused cast mullite brick is made of the bauxite, high quality alumina powder and clay by the fused cast method. It is mainly used in the flue.

Fused chrome corundum brick

Fused chrome corundum brick contains 28.3% Cr2O3, 58.3% Al2O3, and 5.2% MgO and Fe2O3. Its bulk density is 3.4g/cm3. It is used as the flue interface brick of the heat exchanger.

Besides the refractories mentioned above, difference types of fireclay brick and insulation brick are used in the outside layer of the furnace.